Xintema emulsion
Release Date： The Column：The German synthomer carboxylic styrene butadiene latex
Xintema emulsion |
||||||||
| TRADE NAME | TYPE | MFFT（℃） | Tg（℃） | Solid content | PH（±0.5%） |
VISCOSITY （mpa.s） |
Applied advantages | Applied range |
|---|---|---|---|---|---|---|---|---|
| SB 29Y57 | Carboxylic styrene butadiene latex | 0 | -1 | 47 | 10 | 100-500 | Universal, cement compatibility is good;Excluding ammonia;Excellent stability for mortar application (is not affected by cement hardening speed);Excellent cohesive force, flexural strength and compressive strength. | Modified mortar, concrete repair mortar, joint adhesive, sealant, primer, cement anti-corrosion coatings. |
| SB 29Y58 | Carboxylic styrene butadiene latex | 0 | -5 | 48.5 | 8 | 30 | Universal, cement compatibility is good;Excluding ammonia;Excellent stability for mortar application (is not affected by cement hardening speed);Excellent cohesive force, flexural strength and compressive strength. | Modified mortar, concrete repair mortar, joint adhesive, sealant, primer, cement anti-corrosion coatings. |
| SB 30Y60 | Carboxylic styrene butadiene latex | 20 | 14 | 47 | 10 | 30-300 | Universal, cement compatibility is good;Used in rigid cement products;Excellent cohesive force, compression strength;Meet the ASTM C1042. | Repair mortar, polymer cement concrete, plaster, ceramic tile glue, primer. |
| SB 29Y41 | Carboxylic styrene butadiene latex | 0 | -8 | 47 | 10 | 90 | Can be used directly (including defoaming agent), excluding ammonia and improve mortar properties () is not affected by cement hardening speed, excellent compressive strength of mortar, reduce shrinkage, improving wear resistance, good surface effect. | Industrial floor leveling layer (such as warehouse, workshop, garage). |
| SB 60B11 | Butyl benzene latex | 0 | 7 | 50 | 9.5 | 50-250 | Water is extremely low, very low volatile, excellent crack bridging masked for performance, excellent packing compatibility, satisfy the ETAG 022 regulations and DIN EN 14891 standard. | Low odour moistureproof coating. |
| SB 50B30 | Butyl benzene latex | 0 | -6 | 50 | 8.9 | 50-300 | Extremely low volatility, excellent crack bridge performance, excellent packing compatibility, reach the standard JC/T864-2008. | Moistureproof film general makings. |
| 76M10 | Butyl benzene latex | - | -8 | 50 | 6 | 100-350 | Low residual smell. | Used in woodworking glue to improve the water resistance, heat resistance and other properties. |
| 79Q10 | Butyl benzene latex | - | 4 | 50 | 6 | 100-350 | Low residual smell. | Used in woodworking glue to improve the water resistance, heat resistance and other properties. |
| B | Neoprene latex | 0 | -41 | 58 | 13 | 40-120 | High elastic hydrophobic polymers, has good compatibility with emulsified asphalt, using the latex modified asphalt waterproof coating has outstanding flexibility and tensile strength, excellent water resistance, excellent aging resistance and durability, low temperature flexibility is very good, high temperature resistance. | Anionic emulsified asphalt modified waterproofing system,, hot mix asphalt of emulsified asphalt. |
| K | Neoprene latex | 0 | -41 | 57 | 2 | 100-150 | High elastic hydrophobic polymers, has good compatibility with emulsified asphalt, using the latex modified asphalt waterproof coating has outstanding flexibility and tensile strength, excellent water resistance, excellent aging resistance and durability, low temperature flexibility is very good, high temperature resistance. | Cationic emulsified asphalt modified waterproofing system,, hot mix asphalt of emulsified asphalt. |
| X4002 | Pure acrylic emulsion | 0 | -41 | 59.5 | 2.5 | 1000 | High solid content, excellent flexibility, even in freezing conditions, outstanding crack masked for bridging function, saponification resistance is strong, does not contain solvents or plasticizer, excellent uv resistance | Outdoor or indoor use two-component waterproof coating, high flexible cement ceramic tile adhesive, flexible caulking glue elastic additives. |
| R8300 | The styrene acrylic emulsion | 0 | -10 | 57 | 7 | 700-1700 | Extremely high flexibility and resistance to water and good compatibility with cement. | JS waterproof coating, joint sealant, putty glue. |
| R472 | The styrene acrylic emulsion | 0 | -10 | 57 | 7 | 500-3500 | Excellent adhesion and various concrete substrate, at the same time also has a very superior cement and paint, packing adhesive force.After the film showed extremely high flexibility and resistance to water. | The elasticity of the surface of the cement mixture and compounds.It is also applied to the potable water system. |
| AE 4522 | The styrene acrylic emulsion | 18 | 22 | 50 | 7.5 | 350 | Silane modification, damp conditions bond is excellent, good water resistance, good workability. | Vertical metope ceramic tile adhesive (D2), water resistant primer for mineral base material. |
| AE 4530 | The styrene acrylic emulsion | 19 | 26 | 50 | 7.5 | 100 | Silane modified, with mineral base material or oxide class packing crosslinking, damp conditions excellent cohesive force, water resistance is good, do not contain ammonia, meet EN12004 (D2 CTA) requirements. | Low odor water resistant vertical metope ceramic tile adhesive (D2). |
| AE 3020 | The styrene acrylic emulsion | 0 | -2 | 50 | 7.5 | 250 | The silane modification and contains no solvents or plasticizer, excellent resistance to water, crosslinking with base material, damp conditions excellent cohesive force. | Flexible tile adhesive;One-component waterproof coating (external);Flexible anti-cracking coatings. |