Italian SAPICI alkyd resin
|
|
ITEM
|
TYPE
|
COLOR (Fe-Co)
|
NV (±2,%)
|
VISCOSITY (mPa.s.25°C)
|
OH VALUE (±5,原液)
|
PROPERTIES & APPLICATION
|
|
HS129
|
fatty acid
|
≤3
|
60
|
6500-15000
|
60
|
Solvent release and extinction is good, suitable for single as a matte paint, used for primer can improve grinding, can quickly achieve a better surface hardness and flow.
|
|
HS129-70X
|
fatty acid
|
≤3
|
70
|
45000-65000
|
70
|
|
HS130
|
fatty acid
|
≤3
|
50
|
1400-2300
|
45
|
Solvent release sex and extinction is good, suitable for making dumb smooth paint alone, and high flexibility, resin primer.
|
|
XP139
|
fatty acid
|
≤3
|
70
|
20000-38000(23℃)
|
85
|
Quick drying, excellent fullness, flow property, transparency, good solvent release, suitable for PU matte black paint and primer.
|
|
XP5528
|
fatty acid
|
≤3
|
70
|
40000-60000
|
85
|
A good matte configuration and solvent release, dry faster, good flow flat and dry film transparency, suitable for PU dumb smooth paint.
|
|
XP5380
|
fatty acid
|
≤3
|
70
|
22000-37000
|
110
|
Good solvent resistance and the bit bottom resistance, dry faster, good flexibility, grinding resistance, suitable for PU bite prevention, solvent resistant primer.
|
|
1234
|
castor
|
≤3
|
60
|
1400-2300
|
90
|
Flexibility, with excellent stability, is suitable for do have strict request for indiscrete primer, increase the flexibility of the modified resin, also can be used for the nitro or acid curing system.
|
|
2039
|
modified castor oil
|
≤4
|
50
|
4500-10000
|
80
|
Quick drying, high hardness, high fullness, used to prevent subsidence, various kinds of high-grade primer paint.
|
|
AP572
|
synthetic fatty acid
|
≤1
|
80
|
7000-12000(23℃)
|
110
|
High fullness, resistance to yellow degeneration, can improve the hardness and flexibility of the lacquer that bake, suitable for high gloss finish.
|
|
AP575
|
synthetic fatty acid
|
≤1
|
80
|
35000-45000(23℃)
|
120
|
Quick drying, high gloss, high hardness, suitable for fast drying, high gloss finish.
|
|
HG3
|
synthetic fatty acid
|
≤1
|
80
|
35000-45000
|
115
|
High gloss, high hardness, high fullness, lower yellow degeneration, suitable for high-grade high gloss finish, used for system to improve the coating film toughness.
|
|
HG6
|
synthetic fatty acid
|
≤1
|
80
|
35000-45000(23℃)
|
120
|
High gloss, high hardness, high fullness, lower yellow degeneration, suitable for high-grade specular paint, used for system to improve the coating film toughness.
|
|
HG7
|
synthetic fatty acid
|
≤1
|
80
|
40000-50000
|
120
|
High gloss, high hardness, high fullness, good resistance to yellow degeneration, suitable for PU varnish and color paint.
|
|
XP2268
|
synthetic fatty acid
|
≤1
|
80
|
3000-6000(23℃)
|
110
|
High gloss, fullness, good pigment wetting, flow property, excellent resistance to yellow modified acrylic polyol, suitable for high quality glossy white paint, white paste, or use in hydroxyl acrylic system increases luster.
|
|
DP315
|
saturated polyester
|
≤2
|
75
|
17000-25000(23℃)
|
125
|
Quick drying, high hardness, high gloss, good scratch resistance, pressure plate, suitable for the light can be polished finish.
|