VINNAPAS wei solid copolymer emulsion - resistant polyvinyl alcohol as the protection system
|
|
Grade
|
Polymer type
|
Origin
|
SOLID HARDENER
|
VISCOSITY [mpa.s]
|
PH Value
|
Glass Temperature
|
ADVANTAGES
|
|
VINNAPAS® EP724
|
VAc-E
|
Korea
|
55
|
1500-2500
|
4.0-6.0
|
19
|
Good tensile strength, cohesion, and heat resistance.Mixed with polyvinyl acetate homopolymer can achieve higher initial viscosity, curing speed and water resistance.
|
|
VINNAPAS® 320
|
VAc-E
|
Korea
|
56
|
1800-2700
|
4.0-5.0
|
14
|
Standard solid content emulsion, using polyvinyl alcohol as protective colloid, high resistance to water.On the plastic film coating paper and some excellent cohesiveness.With complete hydrolysis or partial hydrolysis of poly (vinyl alcohol) has a unique compatibility.
|
|
VINNAPAS® EP709
|
VAc-E
|
Korea
|
55
|
2700-3700
|
4.0-6.0
|
7
|
High cohesion strength and water resistance.And inorganic filler has excellent compatibility with cement.Has a good bonding performance for hard surface.
|
|
VINNAPAS® EP705A
|
VAc-E
|
Korea
|
55
|
1900-2800
|
4.0-6.0
|
0
|
To different base material surface, including paper, wood, PVC, OPP film.Good Newtonian rheological properties, suitable for high speed packing equipment.
|
|
VINNAPAS® EP705K
|
VAc-E
|
Korea
|
55
|
2900-3900
|
4.0-6.0
|
0
|
To different base material surface, including paper, wood, PVC, OPP film.Good Newtonian rheological properties, suitable for high speed packing equipment.
|
|
VINNAPAS® EP706
|
VAc-E
|
Korea
|
55
|
3500-4500
|
4.0-6.0
|
0
|
Excellent wet viscosity and initial adhesion to different substrate surface bonding, including paper, wood, PVC, OPP film.
|
|
VINNAPAS® EP706K
|
VAc-E
|
China
|
55.5
|
4400-5400
|
4.0-6.0
|
0
|
Is the high viscosity VINNAPAS EP 706 version of the emulsion, the need for special additives and fillers to improve viscosity in order to reduce the cost of total adhesive dispensing.
|
|
VINNAPAS® EP707K
|
VAc-E
|
China
|
55
|
1300-2000
|
4.0-6.0
|
0
|
Low viscosity, high curing speed and good flexibility, is the choice of high speed equipment, have excellent elongation at break and water resistance.
|
|
VINNAPAS® EP710
|
VAc-E
|
China
|
55.5
|
4400-5400
|
4.0-6.0
|
0
|
Low VOC content of multi-function VAE emulsion copolymerization, can be used to make cigarettes by mouth, gum and packaging adhesive.Designed for preparation of low formaldehyde and low residual monomer content of cigarette adhesive latex products, developed to meet the latest standards in China.Have good softness, easy packing, high elongation, fast curing, can clean sex is strong, and good spraying and roller coating performance.
|
|
VINNAPAS® EP711
|
VAc-E
|
China
|
55
|
1300-2000
|
4.0-6.0
|
0
|
Low VOC content of multi-function VAE emulsion copolymerization, can be used to make cigarettes by mouth, gum and packaging adhesive.Designed for preparation of low formaldehyde and low residual monomer content of cigarette adhesive latex products, developed to meet the latest standards in China.Have good softness, easy packing, high elongation, fast curing, can clean sex is strong, and good spraying and roller coating performance.
|